Waterproofing

Two-component cold-applied aromatic polyurea
Seamless, joint-free waterproof membrane.
High elongation and flexibility
Up to 500% elongation and certified crack-bridging (Class A5/B3.2).
Abrasion & impact resistant
Taber abrasion <3000 mg
Impact resistance: Class III (24.5 Nm)
Root and hydrostatic pressure resistance
Certified for green roofs and below-grade waterproofing (100 psi resistance).
UV topcoat compatible
Requires an aliphatic PU topcoat for long-term UV resistance.
Wide application range
Effective from -10°C to +35°C and under ponding water (flat roofs, foundations, terraces, etc.).
Certified & CE marked
ETA 20/0253 under EOTA and EN 13948 (root resistance), with 25-year working life (W3).

Open the container and mechanically mix the product using a low-speed drill (300-450 rpm) to reduce air entrapment and to obtain a homogeneous mixture. Apply the layer with a short nap roller or notched trowel, ensuring a maximum thickness of 1.5 mm (60 mils). The material should be applied undiluted. Allow it to dry completely (drying time may vary depending on weather conditions, approximately 3 hours). Once dried, apply an aliphatic polyurethane resin for UV protection.

Two-component aromatic polyurethane coating
Forms a durable, seamless membrane once cured.
100% solids with low VOC (14 g/L)
Solvent-free and environmentally friendly.
High mechanical performance
Tensile strength >15 MPa
Elongation ±75%
Shore A hardness > 93
Excellent wear and impact resistance
Abrasion: 20 μm wear
Impact resistance >14.7 Nm
Antiskid Certified (Class 3)
Suitable for wet environments with slopes and steps.
CE Marked (EN 13813:2014)
Certified for industrial flooring use in Europe.
High coverage
Up to 980 ft²/kit at 9–10 mils.

Open pails of both components and homogenize each one by mixing equipment at medium speed. Pour component B into the container of component A. Mix thoroughly with an electric mixer at medium speed until a uniform, homogeneous mixture is achieved. If unsure, perform a test application on a small area to verify suitability. Apply the first layer using a brush or short nap roller, ensuring a consumption of 9-10 mils thickness. Once dry, apply the next layer in the same manner. For highly absorbent surfaces or very light colors, a third coat may be required.

Single-Component, Solvent-Based Polyurethane: Moisture-cured, ready-to-use formula—no mixing required.
80–90% Solids Content with VOC Compliance: Delivers a dense, durable film with VOC content between 210–270 g/L.
High Elongation and Flexibility: Over 500% elongation at break (ASTM D412), offering excellent crack-bridging ability.
Outstanding Adhesion Strength: Pull-off strength exceeding 500 psi on both steel and concrete substrates.
Resistant to Ponding Water: Certified for zero-slope roofs and exposed decks where water accumulation occurs.
UV Topcoat Compatibility: Compatible with aliphatic PU resins for added UV resistance and long-term protection.
Certified Waterproofing System: ETA 10/0121 (roof), ETA 21/0734 (bridge-deck), and BBA 16/5340 certifications under EU norms.
Green Roof & Root Resistance Approved: Certified under EN 13948 for anti-root resistance, ideal for vegetated roofs.
Excellent Tensile and Puncture Resistance: Tensile strength up to 695 psi, puncture resistance of 37 lbf, and high Shore A hardness of 86.
Multiple Application Methods:  Can be applied via roller, notched trowel, or airless spray equipment for adaptability on job sites.

Remove dust, dirt, grease, oil, and all other contaminants with proper cleaner/degreaser. Prepare the surface mechanically as per ICRI-CSP2 profile by diamond grinding to ensure removal of laitance, curing agents and sealers. The compressive strength of a newly poured concrete substrate must be at least 25 MPA (3635 psi) after 28 days of cure and at least 1.5 MPA (218 psi) tensile strength. Be careful with condensation (at least 3 degrees of the dew point). All cracks, holes and irregularities must be repaired with a crack filler prior to applying the coating.